Hello all. I have been working with a sulfur deplating cell.
Cell consists of 1 quart container with lead cathode and copper anode basket with a 3amp charger set to 12 volt. I have been working on deplating 3000g of military grade gold plug pins. My question is to find out if anyone has had a problem with their cell working in a very spotty way. By this i mean that some days i can get at least 3 or 4 runs in before the charger will quit charging my electrolyte and i have to stop for the day. Other days i cant even manage to get one run completed before it acts as though i have nothing in the cell at all. And almost always i have to pick through the pins because several are only partially deplated.
I have decanted my electrolyte thinking it may be too saturated but it makes no difference. Any opinions similar experiences would be greatly appreciated.
Cell consists of 1 quart container with lead cathode and copper anode basket with a 3amp charger set to 12 volt. I have been working on deplating 3000g of military grade gold plug pins. My question is to find out if anyone has had a problem with their cell working in a very spotty way. By this i mean that some days i can get at least 3 or 4 runs in before the charger will quit charging my electrolyte and i have to stop for the day. Other days i cant even manage to get one run completed before it acts as though i have nothing in the cell at all. And almost always i have to pick through the pins because several are only partially deplated.
I have decanted my electrolyte thinking it may be too saturated but it makes no difference. Any opinions similar experiences would be greatly appreciated.