In this picture, sorry for the repost.
Help Support Gold Refining Forum:
LOL, " becouse $$$$ are crossing all of you like a BigFoot" read all post again and think about it. I mean there are materials witch looks like scrap and many of scrappers throw it to the trasch stuff. There was nothing about that you are doing nothing or dont know nothing...
I doing this like a hobby becouse I'm intrested and i like it.If somebody tell's me the ball is not round I will tell "you are wrong" no " you are d...." and thats the biggest difference.
Attachments
It appears to be a Miller Table.
Not trying to steal any "thunder" from Kurtak. But, he's busy educating a newbie.
Peace and health,
James
That's not actually true. Changing the substrate does not change the behavior with XRF, just changes the algorithm used to calculate proportions. You can analyze fluids just the same as powder and prepared alloy....you just have to use curve fitting against known samples. Gravimetric analysis always wins, everything else is just a tool with well known limitations.The XRF, XRD, edERX dont show you existation of the PGM becouse its a bimetalic structure witch is changing all of the electric proporties. To mesure the contamination of PGM's in this materials you need use ASA or wet path witch depends what material you need to check.
This is hi tech. eqiupment better then simply old militarny stuff
I'm not really part of this phallus swinging contest, I'm just here for the metals. You posted pictures of boards. I'm pretty positive I've got identical boards in my stash. Take a nice close up picture and tell me exactly what parts to assay and I will. I also happen to have some old military stuff...I'd take it anyday over modern telecom.
kurtak
Well-known member
It sort of a miller table except that the rubber mat I use has small groves in it instead of being a flat rubber mat used in a true miller table
Kurt
kurtak
Well-known member
Per the bold print - first you come on here & tell us that we don't know anything - that we need to start doing our research - because money is crossing our path like bigfoot --- NOW you have the balls to tell us we are dumb
Man - you are really something else - you just can't post something without including an insult in your post
There is NOTHING in ANY of the pictures you have posted that we have not already seen &/or for that matter processed
In other words - you ARE NOT showing us ANYTHING new &/or telling us something we don't already know
& yet you have the balls to come on this forum & tell us ------
we don't know anything - that we need to start doing our research - because money is crossing our path like bigfoot - AND - NOW tell us we are dumb
I am DONE with you - you are not teachable
Oh - wait - your not really trying to teach us - you are try to sell your stuff - but you wont post a selling price
That's because you are looking for a sucker - through email - that will pay 5 - 10 times it's true value --- &/or sell it as many times as possible - to those that contact you through email - with no intent to deliver
Which is why - just like the original poster of this thread - you have to insult us - in the hopes some sucker here - will take the bate - send you money - because if you (the sucker) don't jump on this deal ------
money will cross you path like bigfoot - & you (the sucker) will miss out on the deal of a life time
That's the reason behind the insults - it's to make a sucker believe we don't know anything - so the sucker should listen to you - AND - send you their money
You came to the wrong place to try to SCAM people !!!!!!!!!
Kurt
Man, this escalated quite far.
Do not waste your time on arguing guys, there are more useful things to do
like actual refining or actual selling of these boards
Do not waste your time on arguing guys, there are more useful things to do
like actual refining or actual selling of these boards Facts, not assumptions. Assumptions are insulting in regard to a majority of us in the relative industries, and as members of this forum. Use the search bar, I'm sure you'll find relative threads on your stockpile.LOL, " becouse $$$$ are crossing all of you like a BigFoot" read all post again and think about it. I mean there are materials witch looks like scrap and many of scrappers throw it to the trasch stuff. There was nothing about that you are doing nothing or dont know nothing...
If somebody tell's me the ball is not round I will tell "you are wrong" no " you are d...." and thats the biggest difference.
In regard to the classification of scrappers that you know of, that might be true, but that is not the same here in the states.
Although their of course will be some that don't, a majority of scrappers I know of, separate it like that, and collect it. At the least, they'll get in contact with those of us in the e-waste, resale, refining trades.
The more accurate, classification of those that just throw it away would be the general population globally. Their are many individuals that do not scrap at all, and instead just throw it away, period. There is not enough people informed of what to do, just don't care to recycle, or to learn about consumer electronics in that way.
This is a known global issue, as the amount of e-waste per year is in the range of 57 million tons, and rising.
With that said, no animosity here or in my typing. Just direct, and factual.
You right, I'm not rafiner but simply hobbyst but before that post some big rafiner contact me and now I for the end of rafination proces. In the meantime when waiting I lern about the pirometalurgy in practice and now I done 72g od 90% Rh without using chemicals at two days after workMan, this escalated quite far.
Do not waste your time on arguing guys, there are more useful things to do