Introduction/cry for help/offer?!

[Ahmineholla]

Hello,my name I guess can be E for now, I'm in a terrible but exciting semi flop of attempting to1st( sell my 27lbs 59%iron,20%Pd,20%Au,+/-1% Cu,Ag, with increments 6-8% iridiumPgm) 2nd I attempted oxy acet batch with some enjoyment but other circumstances crashed that attempt.
Now have a positive nitric batch awaiting aide and a positive aqua Regia sizzling away at a small amount of material as well.

I dont have a problem with my first batch it's littered with smb and has turned into Grey mud with white powder all around it with bright yellow blotches and tends to crystallize and seperate over night.
One more note: if I may find an ear interested in participating/ or flat out buying a roll of 27lb 59iron 20pd20au I'm on the forum now and feel open for either instruction or partnership or business opportunity. I'm very proud to post on this forum thank you

 

[Yggdrasil]

Hello,my name I guess can be E for now, I'm in a terrible but exciting semi flop of attempting to1st( sell my 27lbs 59%iron,20%Pd,20%Au,+/-1% Cu,Ag, with increments 6-8% iridiumPgm) 2nd I attempted oxy acet batch with some enjoyment but other circumstances crashed that attempt.
Now have a positive nitric batch awaiting aide and a positive aqua Regia sizzling away at a small amount of material as well.

I dont have a problem with my first batch it's littered with smb and has turned into Grey mud with white powder all around it with bright yellow blotches and tends to crystallize and seperate over night.
One more note: if I may find an ear interested in participating/ or flat out buying a roll of 27lb 59iron 20pd20au I'm on the forum now and feel open for either instruction or partnership or business opportunity. I'm very proud to post on this forum thank you

Welcome in.

First, I don’t have access and financial muscles to pitch in to this kind of endeavours.
Next, I believe it may be easier to get a response if they know where you are located. General area would be enough I guess.

 

[Ahmineholla]

Thank you for your response if in the future if intelligent or accurate methods are useful for my refining attempts I desperately could use a few fine tuning from the outside looking in. 59%iron,18% palladium, 16% gold, 4% rhodium/iridium, 1> Cu,Co,Ag,and few misalaneous underpeecentages. Alloy

 

[Ahmineholla]

I didn't mean to get so exaggerated on one of my posts my fellows I'm sorry about that, but it's is nice to let out some of the tons of stress dealing with precious metals sometimes.
Anyhow before I go into more drama, I currently put my 50%iron,20%gold,20% PGM W/O PLATNIUM(PALLADIUM,IRIDIUM,RHODIUM ONLY) ALLOY

And filled decanter with aquaregia HAD ADDED 50% DISTILLED WATER FIRST THEN THE AQUA REGIA DESPITE WHAT INSANELY LOOKED LIKE A BOIL OVER NOT SURE (sorry for the bold typing) I was lucky enough to have majority of liquid remain but I added more nitric and water to the white bluish spillover and put it all back into the decanter 3 days later all metal has been riddled with strpes, holes, and decolored from shiny silvery colored to flate Grey matte colored like wet concrete or cement looking when wet. The liquid is deepest blue and purple. For some reason I'm a bit stopped in my tracks due I just pit liquid aside or add aquaregia to the liquid again or just Muratic. And for the metal still in decanter do I hit it again with aqua Regia or try soaking in muratic or what. Any understanding of this purple blue black liquid and why my metal is all holed through everywhere will be excellently respected. Thank you will post pictures shortly