I processed a couple thousand pins that were gold plated the full length. When I got to the cupeling part it seemed that the base metals were oxidizing nicely and getting absorbed. Eventually, my button was soft, dense, and 'rose gold' in color. Did this mean there was just some copper left to go? The 'baser' base metals leave first, right? Well, fresh bone ash cupel and back into the furnace. I don't know if I turned the propane up too high, left it too long, or what, but that cupel was fully spent and also empty. What happened?
How hot does a cupel furnace need to be? Can it get hot enough that PMs are oxidized into bone ash cupels?
- Thread starter zamistroe
- Start date
Help Support Gold Refining Forum:
I have two questions here.
Why did you select cupelling when you have a Copper rich material?
How much in weight was these pins and what kind of pins?
Generally copper rich materials benefit from scorification in assay quantities or in production quantities some form of parting to dissolve away the copper selectively.
My understanding was all the non PM would oxidize and leave just Au and the like. Not so?
I had 12 oz of the sort found in Amphenol connectors. They were new old stock, just bare pins in a bag.
Ok, caused by too much time, heat, or something else? What process is used for retrieval?
I've not heard of Bugbee. Thanks, I'll check into it.
I should also mention, I added lead to the the button before the final firing. About an equal weight. But that's not scorification I guess. I'm not clear on the difference between scorification and cupelling.